305 stainless steel sheet

305 stainless steel sheet

Verified Supplier

Verified stockists and suppliers

available 9 cars

305 stainless steel sheet

Above are verified UNS S30500 hot rolled plate suppliers

305 stainless steel sheet specification

305 stainless steel sheet specifications

Contact the reliable 305 stainless steel sheet suppliers in the UAE listed above for bespoke sizes.
Size range of ASME SA 240 TP 305 plate and sheet 1.4303 stainless steel sheet thickness SS 305 plate thickness
  • Width: 914mm to 1524mm
  • Length: 300mm to 6000mm
Thickness: 0.4mm to 6.0mm Thickness: 3.0mm to 100mm
ASTM A240 TP 305 sheets surface treatment A240 type 305 plates ASTM standard/American standards ASME SA 240 Grade 305 plate and sheet density
  • PVC Coated
  • Film Coated
  • Coated
  • Color Coated
  • Galvanised
  • ASTM A240/ A240M Type 305
  • ASTM A412/ A412M Type 305
  • ASTM A480/ A480M – SS 305 flat rolled sheet
  • ASTM A263/ A263M – SS 305 Clad Plate
  • ASTM A666/ A666M – SS 305 Annealed/ cold worked sheet
  • ASTM A177/ A177M – SS 305 high strength plate
  • ASTM A895/ A895M – SS 305 free machining plate
8 g/cm3
ASTM A240 Gr 305 sheet maximum operating temperature ASME SA 240 Gr 305 sheet and plate melting point 1.4303 AISI 305 plates bending method
1149 to 1260°C 1454°C
  • Press braking
  • Roll bending
  • Rotary bending
European standard Hardness range of INOX 305 plate 305 ss plates and sheets lifespan
  • EN 10088 -2 (Technical delivery conditions)
88 HB Upto 30 years
Type 305 stainless steel sheet edges Most popular EN 1.4303 plate types Manufacturing methods of AISI 305 plates
  • round
  • rolled
  • deburred
  • slit
  • square
  • broken corner
  • v edge
  • custom
  • 305 SS Sheet
  • UNS S30500 Plate
  • ASTM A240 SS 305 Perforated Sheet
  • SA 240 tp 305 Foils
  • EN 1.4303 Coils
  • 305 stainless steel Plain Sheet
  • Type 305 stainless steel Strip
  • ASTM A240 Grade 305 Shim Sheet
  • Steel 1.4303 Chequered Plate

In contrast to other 305 stainless steel sheet suppliers, compare our price and response time.

  • Cold Rolled ASTM A240 SS 305 plate
  • Hot Rolled Inox 1.4303 sheet
SA 240 gr 305 sheets processing EN 1.4303 plates and sheets origin Supply A240 TP305 sheet in following brand
  • Temper pass with cut edge
  • Pickling outside with mill edge
  • Pickling with mill edge
  • Pickling with cut edge
  • Temper pass with mill edge
  • Pickling outside with mill edge
  • US
  • Korea
  • Thailand
  • Indian
  • European
  • Japanese
  • Taiwan
  • Baosteel
  • TISCO
  • Arcelor Mittal
  • VDM
  • POSCO
  • Aperam
  • Jindal Stainless
  • DKC Korea
  • Thyssenkrup
  • Nippon Metal
  • Outokumpu
SUS 305 sheets and plates marking SA 240 SS 305 plates finish SA 240 tp 305 sheet applications
  • Manufacturer logo / name
  • Sizes
  • ASTM/ ASME standard
  • Origin of material
  • Manufacturing date
  • Material grade
  • Embossed
  • Hair line
  • Sand blast
  • Brush
  • Etching
  • 2B
  • 2D
  • BA
  • 8K
  • Mirror Finish
  • Checkered
  • NO.1
  • NO.4
  • NO.8
  • Brushed finish
  • Cryogenic applications
  • Petroleum Industry
  • Food and beverage industry
  • Chemical industry

Buy from the top zero-rejection 305 stainless steel sheet suppliers in South Africa, Middle East, Egypt, US, Oman, and Saudi Arabia.

305 SS plates and sheet standard ASTM A240 SS 305 sheets certification Services of ASTM A240 Grade 305 plates
  • ASTM A167
  • EN10088-2-2005
  • ASME SA240
  • GB/T3280-2007
  • ASTM A240
  • JIS4304-2005
  • Raw Materials Certificate
  • 100% Radiography Test Report
  • Third Party Inspection Report
  • EN 10204/3.1B,
  • Certificate of Origin legalized
  • Cutting
  • Minor Fabrication
  • Rolling
  • Forging
  • Bending
  • Beveling
  • Polish
  • Annealing
  • Shearing
  • Forming
  • Welding
  • Machining
  • Pickling
  • Heat Treatment
  • grinding
  • Plate Leveling

Chat or email are the best ways to get in touch with mentioned 305 stainless steel sheet stockists, stockholders, and distributors for these services.

Packaging of 305 stainless steel sheet sheet SA 240 gr 305 coil plates testing requirements AISI 305 sheets welding method
  • Wooden boxes/ crates/ pallets
  • Industrial packing techniques
  • Big rolls with spools
  • Bundles with plastic wrapping
  • PMI testing
  • Hardness Testing
  • UT testing
  • Packing Condition
  • Dimension Verification
  • Witnessed Chemical Analysis
  • Visual Inspection
  • MIG welding
  • TIG welding
  • Resistance welding
Compare ASME SA 240 TP 305 plate, sheet & coil SUS 305 strips surface Benefits of ASTM A240 Type 305 plates and sheets
  • Sheet thickness: from 0.5 mm up to 6 mm
  • Foil thickness:less than 0.2 mm
  • Plate thickness: at around 6 mm or thick
  • Black Surface
  • Grounded: Bright sheet but rough ; Not precision
  • Machining for plate: Precision & bright ; Little turning scar
  • Turned/ Peeled material: Precision & bright; Little turning scar
  • Polished AISI 305 sheet: Very Bright finish & precision size; No turning scar
  • Good oxidation resistance
  • Good strength
A240 gr 305 plate method of cutting ASME SA 240 Type 305 sheet documentation provided Delivery schedule of 305 stainless steel plate
  • Plasma cutting
  • Laser cutting
  • Oxy-propane flame cutting
  • Waterjet cutting

Direct contact with the above-mentioned 305 stainless steel sheet distributors, dealers, and stockists for those specific cuts

  • Copy of Invoice
  • Copy of Packing List indicating details of Sizes, quantity, weight, thickness etc.
  • Manufacturer’s Mill Test Certificate certifying, Heat No, finish, Chemical Composition, Grade etc.,
  • Country of Origin Certificate (Original)
  • Bill of Lading.
  • Generally it is 7-10 days if its in stock
  • 15-20 days if its not in stock
SS 1.4303 hot rolled plate smelting Forming of ASTM A240 Grade 305 plate ASTM A240 Gr 305 perforated sheet heat treatment
  • EAF+PESR: protective atmosphere Electro Slag Remelting
  • EAF+LF+VD: Refined-smelting and vacuum degassing
  • VIM+PESR: Vacuum induction melting
  • EAF: Electric Arc Furnace
  • EAF+ESR: Electro Slag Remelting
  • Hot rolling process
  • Hot Forging
  • +A: Annealed (soft/ full/ spheroidizing)
  • +N: Normalized
  • +P: Precipitation hardened
  • +AT: Solution annealed
  • +NT: Normalized and tempered
  • +QT: Quenched and tempered (oil/ water)

2B is the most widely used SA 240 gr 305 coil surface finish, View Weight chart of SUS 305 strips

Various types of SA 240 gr 305 plates

ASTM A240 TP 305 sheet

ASTM A240 TP 305 sheet

Type 305 stainless steel plate

Type 305 stainless steel plate

SUS 305 slitting coil

SUS 305 slitting coil

INOX 305 perforated sheet

INOX 305 perforated sheet

EN 1.4303 foils

EN 1.4303 foils

UNS S30500 coils

UNS S30500 coils

ASTM A240 Type 305 thin strips

ASTM A240 Type 305 thin strips

Steel 1.4303 plain sheet

Steel 1.4303 plain sheet

AISI 305 rolling plate

AISI 305 rolling plate

ASME SA 240 Type 305 strip

ASME SA 240 Type 305 strip

A240 gr 305 shim sheet

A240 gr 305 shim sheet

305 SS chequered plate

305 SS chequered plate

Chemical composition of SUS 305 strips

Element Content (%)
Iron, Fe 67
Chromium, Cr 18
Nickel, Ni 12
Manganese, Mn ≤ 2
Silicon, Si ≤ 1
Carbon, C 0.12
Phosphorous, P 0.045
Sulfur, S 0.030

AISI 305 clad plate mechanical properties

Various destructive and non destructive test are performed on AISI 305 clad plate, Exporter listed above of EN 1.4303 chequered plate keep ready stock to dispatch

Properties Metric
Modulus of elasticity 193 GPa
Tensile strength, ultimate 585 MPa
Tensile strength, yield (@0.2%) 260 MPa
Elongation at break (in 50 mm) 50
Shear modulus 86 GPa
Hardness, Brinell 80

ASTM A240 Gr 305 perforated sheet equivalent

EU USA Japan France England Russia
EN JIS AFNOR BS GOST
X4CrNi18-12 (1.4303) 305 SUS305J1 Z1CN18-12 305S19 06KH18N11

EN 1.4303 chequered plate Physical properties

By using laser cutting method max thickness of 12mm can be cut of Type 305 stainless steel slitting coil, PVC coating can be applied on A240 TP305 shims for Decoration, Furniture application
Properties Metric
Melting point 1454°C
Density 8 g/cm3

Thermal properties of A240 TP305 shims

Properties Metric
Thermal conductivity (@0-100°C/32-212°F) 16.3 W/mK
Thermal expansion co-efficient (@0-100°C/32-212°F) 17.3 µm/m°C

Hot working and annealing of INOX 305 material

Hot working Annealing
1149 to 1260°C (2100 to 2300°F) 1010 to 1121°C (1850 to 2050°F)

Thickness and weight of SA 240 gr 305 sheet

ASTM A240 Gr 305 perforated sheet annealed at temperature ranging from 1010 to 1121°C, INOX 305 material is suitable for very severe cold forming operations
Thickness
(mm)
Weight
(kg/m 2)
1.6 12.6
2.0 15.7
2.5 19.6
3 23.6
3.2 25.1
4 31.4
5 39.3
6 47.1
8 62.8
10 78.5
12.5 98.1
15 118
20 157
22.5 177
25 196
30 236
32 251
35 275
40 314
45 353
50 393
55 432
60 471
65 510
70 550
75 589
80 628
90 707
100 785
110 864
120 942
130 1051
150 1178
160 1256
180 1413
200 1570
250 1963