410S stainless steel sheet

410S stainless steel sheet

Verified Supplier

Verified stockists and suppliers

Purchase ASTM A240 Type 410S plate from verified suppliers

410S stainless steel sheet specification

410S stainless steel sheet specification

For custom sizes, please contact the above-mentioned 410S stainless steel sheet suppliers who are situated in the United Arab Emirates.
Manufacturing size range of ASTM A240 Gr 410S plate and sheet 410S ferritic stainless steel sheet thickness ASTM A240 Type 410S plate thickness
  • Width: 914mm to 1524mm
  • Length: 300mm to 6000mm
Thickness: 0.4mm to 6.0mm Thickness: 3.0mm to 100mm
stainless steel 410S sheets surface treatment 410S stainless steel plates ASTM standard/American standards ASTM A240 TP410S plate and sheet density
  • PVC Coated
  • Film Coated
  • Coated
  • Color Coated
  • Galvanised
  • ASTM A240/ A240M Type 410S
  • ASTM A412/ A412M Type 410S
  • ASTM A480/ A480M – SS 410S flat rolled sheet
  • ASTM A263/ A263M – SS 410S Clad Plate
  • ASTM A666/ A666M – SS 410S Annealed/ cold worked sheet
  • ASTM A177/ A177M – SS 410S high strength plate
  • ASTM A895/ A895M – SS 410S free machining plate
7.65 Mg/m3
Stainless steel grade 410S sheet maximum operating temperature Alloy 410S sheet and plate melting point SS 410S plates bending method
1300°F (705°C) 2700–2790° F
  • Press braking
  • Roll bending
  • Rotary bending
European standard Hardness range of ASTM A240 Grade 410S plate AISI 410S plates and sheets lifespan
  • EN 10088 -2 (Technical delivery conditions)
75 HB Upto 25 years
SA 240 Gr 410S sheet edges Different INOX 410S cold rolled plate types Manufacturing technique of Alloy 410S
plates
  • round
  • rolled
  • deburred
  • slit
  • square
  • broken corner
  • v edge
  • custom
  • AISI 410S Sheet
  • SA 240 Gr 410S Plate
  • ASTM A240 Gr 410S Perforated Sheet
  • EN 1.4000 Foils
  • SA 240 Gr 410S Coils
  • UNS S41008 Plain Sheet
  • 410S stainless steel Strip
  • Alloy 410S Shim Sheet
  • 410S ferritic stainless steel Chequered Plate

In contrast to other 410S stainless steel sheet suppliers, compare our price and response time.

  • Cold Rolled SUS 410S plate
  • Hot Rolled UNS S41008 sheet
SUS 410S sheets processing ASTM A240 UNS S41008 plates and sheets origin Supply INOX 410S sheet in following brand
  • Pickling outside with mill edge
  • Temper pass with cut edge
  • Pickling outside with mill edge
  • Pickling with cut edge
  • Temper pass with mill edge
  • Pickling with mill edge
  • Japanese
  • US
  • Korea
  • Indian
  • European
  • Thailand
  • Taiwan
  • Nippon Metal
  • Outokumpu
  • Arcelor Mittal
  • VDM
  • POSCO
  • Aperam
  • Jindal Stainless
  • DKC Korea
  • Thyssenkrup
  • Baosteel
  • TISCO
410S SS sheets and plates marking ASTM A240 Gr 410S plates finish SA 240 Type 410S sheet applications
  • ASTM/ ASME standard
  • Manufacturer logo / name
  • Manufacturing date
  • Material grade
  • Sizes
  • Origin of material
  • BA
  • NO.1
  • NO.4
  • Mirror Finish
  • 2B
  • 2D
  • Checkered
  • etching
  • NO.8
  • 8K
  • Brushed finish
  • embossed
  • hair line
  • sand blast
  • Brush
  • Chemical industry
  • Construction
  • Food processing
  • Petro-chemical plants

Buy from the top zero-rejection 410S stainless steel sheet suppliers in South Africa, Middle East, Egypt, US, Oman, and Saudi Arabia.

Inox 1.4000 plates and sheet standard ASTM A240 SS 410S sheets certification Services of 1.4000 stainless steel plates
  • ASTM A167
  • JIS4304-2005
  • EN10088-2-2005
  • ASME SA240
  • GB/T3280-2007
  • ASTM A240
  • Third Party Inspection Report
  • Certificate of Origin legalized
  • 100% Radiography Test Report
  • EN 10204/3.1B,
  • Raw Materials Certificate
  • Pickling
  • Heat Treatment
  • Polish
  • Annealing
  • Shearing
  • grinding
  • Cutting
  • Minor Fabrication
  • Rolling
  • Forging
  • Bending
  • Forming
  • Welding
  • Beveling
  • Plate Leveling
  • Machining

Chat or email are the best ways to get in touch with mentioned 410S stainless steel sheet stockists, stockholders, and distributors for these services.

Packaging of EN 1.4000 sheet 410S stainless steel hot rolled plate plates inspection list UNS S41008 sheets welding method
  • Big rolls with spools
  • Industrial packing techniques
  • Wooden boxes/ crates/ pallets
  • Bundles with plastic wrapping
  • Packing Condition
  • Dimension Verification
  • UT testing
  • Witnessed Chemical Analysis
  • PMI testing
  • Hardness Testing
  • Visual Inspection
  • MIG welding
  • TIG welding
  • Resistance welding
Compare ASME SA 240 SS 410S plate, sheet & coil INOX 410S material surface Benefits of Steel 1.4000 plates and sheets
  • Sheet thickness: from 0.5 mm up to 6 mm
  • Foil thickness:less than 0.2 mm
  • Plate thickness: at around 6 mm or thick
  • Black Surface
  • Grounded: Bright sheet but rough ; Not precision
  • Machining for plate: Precision & bright ; Little turning scar
  • Turned/ Peeled material: Precision & bright; Little turning scar
  • Polished SA 240 TP 410S sheet: Very Bright finish & precision size; No turning scar
  • Provides high strength
  • Moderate corrosion resistance
  • Remains ductile and soft
AISI 410S plate method of cutting SA 240 Gr 410S sheet documentation provided Delivery schedule of SUS 410S plate
  • Oxy-propane flame cutting
  • Plasma cutting
  • Laser cutting
  • Waterjet cutting

Direct contact with the above-mentioned 410S stainless steel sheet distributors, dealers, and stockists for those specific cuts

  • Copy of Invoice
  • Manufacturer’s Mill Test Certificate certifying, Heat No, finish, Chemical Composition, Grade etc.,
  • Country of Origin Certificate (Original)
  • Bill of Lading.
  • Copy of Packing List indicating details of Sizes, quantity, weight, thickness etc.
  • Generally it is 7-10 days if its in stock
  • 15-20 days if its not in stock
SA 240 Type 410S coil smelting Forming of ASTM A240 SS 410S clad plate SUS 410S slitting coil heat treatment
  • VIM+PESR: Vacuum induction melting
  • EAF: Electric Arc Furnace
  • EAF+ESR: Electro Slag Remelting
  • EAF+PESR: protective atmosphere Electro Slag Remelting
  • EAF+LF+VD: Refined-smelting and vacuum degassing
  • Hot rolling process
  • Hot Forging
  • +P: Precipitation hardened
  • +AT: Solution annealed
  • +A: Annealed (soft/ full/ spheroidizing)
  • +N: Normalized
  • +NT: Normalized and tempered
  • +QT: Quenched and tempered (oil/ water)

ASTM A240 UNS S41008 perforated plate are can be supply in full hard tempered condition, Check size chart of SUS 410S slitting coil

AISI 410S plate types

SUS 410S sheet

SUS 410S sheet

SS 410S plate

SS 410S plate

Stainless steel grade 410S slitting coil

Stainless steel grade 410S slitting coil

SA 240 TP 410S perforated sheet

SA 240 TP 410S perforated sheet

EN 1.4000 foils

EN 1.4000 foils

410S SS coils

410S SS coils

AISI 410S thin strips

AISI 410S thin strips

UNS S41008 plain sheet

UNS S41008 plain sheet

410S stainless steel rolling plate

410S stainless steel rolling plate

INOX 410S strip

INOX 410S strip

Alloy 410S shim sheet

Alloy 410S shim sheet

ASTM A240 Type 410S chequered plate

ASTM A240 Type 410S chequered plate

Chemical composition of UNS S41008 clad plate

Element Content (%)
Manganese, Mn 1.0
Iron, Fe 85
Chromium, Cr 12.5
Silicon, Si 1.0
Carbon, C 0.080
Phosphorous, P 0.040
Sulfur, S 0.030

AISI 410S strips mechanical properties

INOX 410S cold rolled plate is annealed at 649-760°C (1200-1400°F), Above listed stockist can supply SA 240 Gr 410S rolling plate in wide range of thickness

Properties Metric
Elastic modulus 190-210 GPa
Tensile strength 1525 MPa
Yield strength (@strain 0.200%) 1225 MPa
Elongation at break (in 50 mm) 14.50%
Poisson’s ratio 0.27-0.30
Hardness, Rockwell C 45
Hardness, Knoop (converted from Rockwell C hardness) 464
Hardness, Vickers (converted from Rockwell C hardness) 446

Equivalent grade of Stainless steel 410S coil

Grade UNS No Old British Euronorm Swedish SS Japanese JIS
BS En No Name
410S S41008 403S17 X6Cr13 1.4000 X6Cr13 2301 SUS410S

ASTM A240 UNS S41008 perforated plate physical properties

Various testing including MT, UT are performed on Alloy 410S polished plate before dispatching, ASTM A240 Type 410S shims are available in different finishes such as 2B, 2D, bright finish
Properties Metric
Density 7.80 g/cm3
Melting point 1532°C

Inox 410S foil thermal properties

Properties Metric
Thermal conductivity (@100°C/212°F) 24.9 W/mK
Thermal expansion co-efficient (@0-100°C/32-212°F) 9.90 µm/m°C

Size range of SUS 410S plate

SUS 410S slitting coil have slightly poorer weldability compared to other grades, EN 1.4000 coil have width tolerance of +/-2mm
  • Hot Rolled Process – OD 30-500mm ; WT 3-60mm ; L 6-12meter
  • Cold Drawn Process – OD 10-200mm ; WT 0.5-20mm ; L 1-12meter
  • Cold Rolled Process – OD 6-200mm ; WT 0.1-20mm ; L 1-12meter

Alloy 410S coil heat treatment

Annealing 1500-1650°F (816-899°C)
Process Annealing 1350-1450°F (732-788°C)
Hardening 1700-1850°F (927 – 1010°C)