9310 round bar chemical composition and mechanical properties


There are a lot of listed SAE 9310 steel bar stock suppliers in the Middle East countries to be located at pipingmaterial.ae
What is AISI 9310 rod high toughness and core strength?
Low nickel, chromium, and molybdenum alloy are called 9310 alloys. It features a high core hardness in addition to high fatigue strength. This alloy’s best machining form is the normalized and tempered kind. The AISI 9310 Rod is an excellent option for airplane parts due to all of this.
Applications requiring a strong core make use of it. It also possesses high toughness, hardenability, core toughness, and fatigue toughness. When annealed, 9310 Flat Bar exhibits strong ductility, machinability, and cold-working properties.
With sufficient stock of AISI 9310 steel rod, receive a discount in Dubai
What is SAE 9310 hex bar used for?
9310 Alloy Steel Round Bar made of nickel, chromium, and molybdenum is called 9310 Alloy Bar. It features a high core hardness in addition to high fatigue strength. This alloy’s best machining form is the normalized and tempered kind. The SAE 9310 Hex Bar is an excellent option for airplane parts due to all of this.
It’s a terrific option for lifters who wish to benefit from a deadlift and also athletes who compete in non-barbell sports. And all of that without spending the extra time required to perfect a straight-bar deadlift.
Under tempered and quenched conditions, 9310 tool steel flat bar exhibits good weldability properties
What is peeled and reeled 9310 alloy steel bar?
Peeling is the removal of a bar’s outer surface with a rotating tool. Surface flaws are more profound and related to the bars’ diameter; these flaws are removed via peeling, where a cut is made as needed. There are two sorts of bright bars: cold drawn and peeled. The Hot Rolled Bars in a Cold Drawn Bright Bar are pickled and drawn through a Tungsten Carbide Die as Cold Rolled; heating is unnecessary. Hence the name Cold Drawn Bright Bar
Chromium-Nickel-Molybdenum alloy AMS 6265 Forged Bar is used for carburizing aircraft parts. High core strength and toughness can be obtained by users, along with high case hardness. It is suitable for usage in relatively large cross-sections due to its high alloy content. Second, to produce UNS 93106 Flat Bar, Hot Rolled Bar is passed into a turning machine where the surface is turned to the desired diameter. This cold technique does not need heating in the 9310 Alloy Steel Bar. For specific purposes, Bright Bars can be further ground and finished.
AISI9310 alloy steel hex bar standard sizes of 3 m, 4 m, and 6 m lengths offer free shipping
UNS 93106 flat bar tolerances
Tensile strength |
820 MPa |
119000 psi |
Yield strength |
450 MPa |
65300 psi |
Elastic modulus |
190-210 GPa |
27557-30458 ksi |
Poisson’s ratio |
0.27-0.30 |
0.27-0.30 |
Elongation at break (in 50 mm) |
17.30% |
17.30% |
Hardness, Brinell |
241 |
241 |
Hardness, Knoop (converted from Brinell hardness) |
265 |
265 |
Hardness, Rockwell B (converted from Brinell hardness) |
97 |
97 |
Hardness, Rockwell C (converted from Brinell hardness) |
22 |
22 |