JETHETE M152 round bar

Jethete steel rod suppliers in UAE

JETHETE martensitic stainless steel is an AOD ESR, or AOD VAR melted alloy with additional alloying elements. This gives it good strength and temper resistance at temperatures up to 1000 degrees Fahrenheit. This grade can be heat treated to various strengths, just like the JETHETE M152 Round Bar.

Or, to put it another way, it is martensitic stainless steel with a 12 percent chromium content that is nitrogen-bearing and hardenable. It also has excellent creep and corrosion resistance, aside from this. JETHETE M152 Square Bar is a hardened, tempered steel with excellent toughness, ductility, and creeps rupture characteristics. The same can temper resistance at temperatures up to 1040° F (560° C).

Jethete M152 Round Bar sizes, specification, chemical composition and mechanical properties

Find reliable suppliers of m152 alloy flat bar in the Middle East and Asia, also check heat treatment

JETHETE M152 Round Bar can be easily bent, stretched, or spun after annealing as long as feeds and speeds are maintained. In the austenitic range, usually between 1040 and 1100°C, It is normalized and then cooled to room temperature. Due to the high Cr content (13 percent Cr), a martensitic transformation is possible with air cooling. Also, when ASTM A565 Jethete M-152 Hex Bar alloy is treated as follows, it forges flawlessly.

The part must first be heated to 760–788 °C (1400–1450 °F), then rapidly superheated to 1121–1150 °C (2050–2102 °F). Let the metal cool at temperatures above 788 ° C at 1450 ° F before the forge. After forging, the part is cooled at 100 ° C before it is quickly tempered at 1256-1292 ° F (680-700 ° C). To enter the final part, which has been neglected, let the air cool at room temperature.

Check the jethete m152 steel square bar price list in Dubai

Application of M152 alloy bars

Additionally, when machined, this alloy maintains constant feeds and speeds and exhibits high-notch tolerance and favorable thermal expansion coefficients. In high-stress environments, such as turbine blades and turbine discs in the aerospace industry, M152 Alloy Bars are used. The answer lies in the excellent mechanical properties at higher temperatures and good machining properties.

Due to its exceptional creep rupture strength and corrosion resistance, Stainless Steel Jethete M-152 Round Bars are frequently used. For a variety of unusual applications, it is the most diversified one, such as:

• Fasteners
• Drilling machinery
• Mechanical gears
• Landing gear for aircraft and Royce Jet Engines
• Turbine blades under extreme stress

ASTM A565 jethete m-152 hex bar should be corrosion resistant for a specified application or environment

What type of material is AMS 5718 rod?

AMS 5718 is a specification of Jethete M152, a nitrogen-hardenable martensitic alloy containing 12% chromium. This specification exhibits high strength at elevated temperatures and excellent ductility. For this reason, AMS 5718 Rod is an excellent choice for parts used as structural components such as washers, screws, bolts, and rings.

The same is available in 1.4933 Round Bars, forgings, coils, and tubes. It is supplied in the annealed condition, which means it can be further heat treated to achieve the desired properties.

Find require sizes and lengh of 1.4933 round bars

What is BS S151 flat bar used for?

British Standard (BS) steel specifications, grades, and designations are developed by staff at the BSI (British Standards Institute). BS S151 Flat Bar is the British Aerospace standard for stainless steel alloy. S151 is tempered steel with a typical upper-temperature limit of 560°C and is corrosion and creep-resistant.

It combines excellent toughness and creeps rupture properties for highly loaded turbine blades, washers, screws, bolts, and rings. The maximum cross-section of the S151 is 150mm (6″). UNS S64152 Forged Bars are usually supplied in their final heat-treated condition. However, it is also available in thicker sizes with softer materials.