Monel K500 round bar

Monel K500 Round Bar

An alloy of nickel and copper that can be precipitation hardened is K500. In terms of corrosion resistance, Monel K500 Round Bar is comparable to Alloy 400 but offers greater yield and tensile strength. In other words, it is a corrosion-resistant Nickel-Copper alloy that can age and harden.

Monel K500 Flat Bar is frequently used in applications with highly corrosive conditions. Due to its strength and other Monel steel characteristics, this metal typically costs much more than stainless steel.

Verified Supplier

available 3 cars

Alloy K500 hex bar and Monel k500 flat bar suppliers in UAE

Monel k500 round bar specifications


Monel k500 round bar specification

The top 10 Monel K500 round bar suppliers in the United Arab Emirates may create custom drawings
WNR 2.4375 round bar size ASTM B865 UNS N05500 flat bar size ASTM B865 N05500 hex bar size
3-~800mm
  • Width: 10 milimeter – 500 milimeter
  • Dia: 3 milimeter-~800 milimeter
2-100mm A/F
Alloy K500 rod ASTM Standard DIN 2.4375 square bar size Nickel alloy K500 angle bar size
  • ASTM B865
  • ASME B865
4 to 100mm 3 X 20 X 20 milimeter~12 X 100 X 100 milimeter
Monel alloy K500 rectangular bar supply state Alloy K500 bars standards Werkstoff NR. 2.4375 bright bar finish
  • Hardened strain
  • Solenoid quality
  • Trailed center less ground & polished
  • Smooth Turned & Polished
  • Annealed
  • Turned & rough polished
  • The strain Hardened
  • Peeled and polished
  • ASME SB-865
  • AMS 4676
  • QQ N 286
  • Mirror
  • Polishing
  • Hairline
  • Pickled
  • Peeled
  • Black
  • Bright
SB 865 UNS N05500 rounds melting point QQ N 286 shaft density Alloy K500 billet temperature range
1350 °C (2460 °F) 8.8 g/cm3 1300-1350°C
Alloy K500 rod surface Monel alloy K500 bar stock value added services Supply UNS N05500 polished bar in following brand
  • Cold Drawn
  • Hot Rolled Pickled
  • Polished
  • Hairline
  • Bright
  • Sand Blasting
  • Finished
  • Special packaging
  • NORSOK certified stock on select alloys
  • Turnkey inventory stocking programs
  • ISO Certified
  • ASTM; ASME; ANSI; EN; DFAR compliant
  • Same day cutting capability
  • Trepanning, Grinding, PSQ, and Turned, Ground & Polished Bar
  • 24 hr call out service
  • Custom cutting round bar to 16″
  • Testing and secondary heat-treating services

To speak with the Monel K500 round bar stockists, stockholders, and distributors of these services directly, use chat or
email.

  • Tubacex Tubos Inoxidables S.A., Spain
  • Sumitomo Metals, Japan
  • Kobe Special Tube, Japan
  • Special Metals USA
  • Nippon Steel Corporation, Japan
  • Seah Steel Corporation, Korea
  • Sanyo Special Steel, Japan
  • Schoeller Bleckmann, Austria
  • BOHLER
K500 Monel cold drawn bar maximum operating temperature ASTM B865 UNS N05500 bright drawn round bar common trade names Hardness range of ASTM B865 cold finished round bar
up to 1000°F (538°C) Monel k500® 27-35
Most selling k500 round bar types ASME SB-865 hot rolled bars condition Manufacturing methods of Monel K500 bar
  • ASTM B865 UNS N05500 flat bar
  • DIN 2.4375 square bar
  • ASTM B865 N05500 hex bar
  • Alloy k500 round bar
  • Monel alloy K500 rectangular bar
  • ASTM B865 N05500 bright bar
  • Alloy K500 rod
  • QQ N 286 shaft
  • SB 865 UNS N05500 rounds
  • Monel alloy K500 billet
  • K500 bloom
  • B865 UNS N05500 bar stock
  • AMS 4676 forged round bar
  • QQ N 286 cold drawn bar
  • DIN 2.4375 polished bar
  • QQ N 286 bright drawn round bar
  • Nickel Alloy K500 cold finished round bar
  • Monel Alloy K500 hot rolled bars
  • UNS N05500 annealed bar

Compare our response time and price to those of other Monel K500 round bar stockists.

  • Hardened & tempered
  • Annealed
  • Precipitation hardened
  • Hot Rolled
  • Centerless Grinding
  • Forged
  • Cold Drawn
  • Grinding
Certification of Monel K500 annealed bar Origin standards of ASTM B865 forged bar K500 Monel hexagonal bar features
  • Fumigation Certificates
  • Third Party Inspection Report
  • DFARS compliant
  • Raw Materials Certificate
  • EN 10204/3.1B, EN 10204 3.1 and EN 10204 3.2 Material Test Certificates (MTC)
  • Laboratory Test Certificate from Govt. Approved Lab
  • Heat Treatment Charts
  • Form A for Generalized System of Preferences (GSP)
  • Surface roughness measurement
  • HS Code Commercial Invoice
  • Moisture testing report
  • Russia Standard
  • American Standard
  • Janpanese Standard
  • European Standard
  • Superior fatigue resistance and erosion resistance
  • Less ductile and workable
  • Requires age hardening after forming or welding
  • Non-magnetic
  • Significantly higher strength and hardness
  • Precipitation-hardened alloy (multi-phase) with additions of aluminum and titanium
B865 UNS N05500 forged cold drawn bar benefits Alloy K500 precision rod marking K500 peeled round bars applications
  • Extends equipment life due to superior durability
  • Preferred in high-pressure and high-temperature environments
  • Ideal for applications demanding high strength and resistance to fatigue and erosion
  • Nominal Size
  • Heat Number
  • Manufacturer’s Name or Custom Logo – on request
  • Schedule or Wall Thickness
  • Material Grade
  • Specification
  • Method of Manufacturing
  • Impellers and pump shafts
  • Oil and gas well components
  • Marine propeller shafts
  • High-pressure valves and fittings
  • Sour gas and high-temperature environments
  • Aerospace and defense applications

These businesses have extensive expertise supplying the product to nations including Saudi Arabia, the Middle
East, Egypt, South Africa, and USA. They are legitimate distributors and Monel K500 round bar suppliers in
the UAE.

DIN 2.4375 forged round bar documentation offered WNR 2.4375 rod shape ASTM B865 UNS N05500 flat bar tolerances
  • Bill of Lading.
  • Copy of Packing List indicating details of Sizes, quantity, weight, thickness etc.
  • Manufacturer’s Mill Test Certificate certifying, Heat No, finish, Chemical Composition, Grade etc.,
  • Country of Origin Certificate (Original)
  • Copy of Invoice
  • Hollow
  • Round
  • Square
  • Rectangular
  • Hexagonal
  • H8
  • H9
  • H10
  • H11
  • H12
  • H13
  • K9
  • K10
  • K11
  • K12 or custom
ASTM B865 N05500 hex bar payment term DIN 2.4375 square bar AMS Monel alloy K500 rectangular bar lifespan
  • Paypal
  • TT
  • West union
  • LC
AMS 4676 Over fifty years
Alloy k500 round bar inspection checklist ASTM B865 N05500 bright bar packaging ASME SB-865 bloom delivery time
  • Mechanical test
  • Chemical test
  • Destructive test
  • Non destructive test
  • Flaring Test
  • Visual inspection test
  • Third party inspection test
  • PMI test
  • Nabl approved lab test

Effective and brief communication of the test with the above-specified distributors, dealers, and Monel K500 round bar
stockists

  • PE Fabric Bundles
  • Custom
  • Crates (steel/wooden)
  • Wooden Boxes
  • Special crates for with each radius separated
  • Wrapped in plastic or standard seaworthy export packing
  • Bundles (hexagonal)
  • Generally it is 7-10 days if its in stock
  • 15-20 days if its not in stock

Get connected with trusted and genuine ASTM B865 UNS N05500 rod suppliers in the middle east countries

ASTM B865 N05500 hex bar weight calculation formula

Bar Size Diameter (mm)
5 5
5.5 5.5
6 6
7 7
8 8
9 9
10 10
11 11
12 12
14 14
16 16
18 18
20 20
22 22
25 25
28 28
32 32
36 36
40 40
44 44
50 50

ASTM B865 N05500 hex bar weight calculation formula

Type Formula
ASTM B865 N05500 square bar Size (mm) X Size (mm) X 0.00788 = Wt. per Mtr.
K500 Monel hex bar Size (mm) X Size (mm) X 0.00680 = Wt. per Mtr.
K500 round bar Diameter (mm) X Diameter (mm) X 0.00623 = Wt. per Mtr
ASTM B865 N05500 flat bar Width (mm) X Thickness (mm) X 0.00798 = Weight per Mtr.

DIN 2.4375 square bar hs code

Grade HS Code
Alloy K500 75052200

SB 865 UNS N05500 rounds mechanical properties

Properties Value
Tensile strength 1100
Yield Strength 790
Elongation 20%

Physical properties of Monel alloy K500 rectangular bar

Physical Property Value
Density 8.8 g/cm3
Melting Point 1350 °C (2460 °F)
Modulus of Elasticity 160 GPa
Thermal Conductivity 17.8 x W/m.K

Technical information of QQ N 286 shaft

Alloy K500 UNS N05500 ASTM B865

K500 bright bar material equivalent

Standards Country Value
UNS North America N05500
WNR Russia 2.4375
ASTM America B865
ASME Australia SB-865
JIS Japan
BS United Kingdom
GOST Russia
AFNOR France
EN Europe
AMS United States 4676
ANSI America
SAE United States
AS Australia
DIN German 2.4375

ASTM B865 UNS N05500 flat bar tolerances

Type of Monel K500 Bars Sizes (milimeter) Sizes (Inches) Tolerance of Monel K500 Bars ISO
Polished and Peeled 40.00 to 150.00 1.50” to 6.00” h11, ASTMA-484 h11-DIN 1013
Ground and Cold Drawn 10.00 to 75.00 5/6” to 2.50” h8-h9-h10-h11
Ground and Peeled 20.00 to 50.00 3/4″ to 2.00” h9-h10-h11, ASTM B408
Polish and Cold Drawn 3.00 to75.00 1/8” to 3.00” h8-h9-h10-h11, ASTM B408

Monel k500 round bar tolerance

Chemical composition of Alloy K500 rod

Grade Nickel Iron Carbon Manganese Silicon Copper Aluminum Sulfur Titanium
Alloy K500 63.0 0.5 – 2 0.25 1.5 0.5 27.0 – 33.0 2.3 – 3.15 0.010 0.35 – 0.85

Monel k500 round bar properties

k500 Monel bar weight chart

Size (millimeter) Weight per
metre (kilogramme)
Size (millimeter) Weight per
metre (kilogramme)
20 x 20 x 3 0.88 50 x 50 x 10 7.11
25 x 25 x 3 1.12 60 x 60 x 5 4.58
25 x 25 x 5 1.78 60 x 60 x 6 5.40
25 x 25 x 6 2.09 60 x 60 x 10 8.69
30 x 30 x 3 1.35 70 x 70 x 6 6.35
30 x 30 x 5 2.17 70 x 70 x 10 10.30
30 x 30 x 6 2.56 75 x 75 x 6 7.37
40 x 40 x 3 1.83 75 x 75 x 10 11.95
40 x 40 x 5 2.96 80 x 80 x 6 7.89
40 x 40 x 6 3.51 80 x 80 x10 12.80
50 x 50 x 3 2.30 100 x 100 x 6 9.20
50 x 50 x 5 3.75 100 x 100 x 10 15.0
50 x 50 x 6 4.46

Monel k500 round bar weight chart

Monel Alloy K500 hex bar size chart

Hex bar Monel K500 weight per foot K500 Weight per 12-foot Hex bar Dimensions of Monel Alloy K500 Hex Bar in Inches
0.104 1.248 3/16″
0.180 2.160 1/4″
0.290 3.480 5/16″
0.625 4.920 3/8″
0.560 6.72 7/16″
0.740 8.880 1/2″
0.930 11.16 9/16″
1.150 13.80 5/8″
1.390 16.68 11/16″
1.660 19.92 3/4″
1.950 23.40 13/16″
2.300 27.60 7/8″
2.625 31.20 15/16″
2.90 34.80 1″
3.30 39.60 1-1/16″
3.700 44.40 1-1/8″
4.625 55.20 1-1/4″
5.100 61.20 1-5/16″
5.625 67.20 1-3/8″
6.100 73.20 1-7/16″
6.625 79.20 1-1/2″
7.800 93.60 1-5/8″
9.030 108.36 1-3/4″
10.400 124.80 1-7/8″
11.80 141.60 2″
14.920 179.04 2-1/4″
16.920 203.04 2-3/8″
18.42 221.04 2-1/2″
26.53 318.36 3″

Monel k500 round bar size chart

Delivery time and location for k500 round bar

Export to Price variations and estimated delivery
Bahrain 5 % extra | 9 days
Kuwait 5 % extra | 10 days
Singapore 5 % extra | 8 days
Azerbaijan 5 % extra | 30 to 45 days
Egypt 5 % extra | 18 days
Turkey 5 % extra | 21 days
Libya 5 % extra | 45 to 60 days
Nigeria 5 % extra | 30 days
Germany 5 % extra | 20 days
Poland 5 % extra | 45 days
Finland 5 % extra | 45 days
Sweden 5 % extra | 45 days

Purchase monel K500 material and K500 monel alloy rounds at discounted costs from reliable and certified suppliers in UAE

Doctor blades, scrapers, pump parts, cable wrap, oil well drill collars, marine instruments, springs, valve trays, submarine parts, and electronic components are all common uses for K500-based grade steels.

The elements that makeup K500 Round Bar are as follows:

  • 63% Nickel (plus Cobalt)
  • 0.25% Carbon
  • 1.5% Manganese
  • 2% Iron
  • Copper 27-33%
  • Aluminum 2.30-3.15%
  • Titanium 0.35-0.85%

Propellers, pump shafts, and components for centrifugal pumps all use the monel alloy k500 Shaft in their manufacturing processes for oil and gas.

The method of observation of the metallographic structure of the type mentioned above of Monel/steel built-up welding interface. It uses distilled water to clean the ASTM B865 UNS N05500 Rod. Use lacquer solution to get rid of paint stains. The corrosion resistance of this nickel-copper alloy to acids is exceptionally high and can be hardened through precipitation techniques.

Daily cleaning is different from periodic cleaning. This service will schedule a cleaner to visit your property regularly. It might happen once a week, once a month, or even less frequently.

Gas turbine engine components that withstand high temperatures and have high strength frequently use Alloy K500 Square Bar. Monel was advertised as a white metal more robust than steel, corrosion-resistant than iron, and more brilliant than nickel.

Alloy K500 Hex Bar has a maximum temperature of 1000 degrees Celsius, almost twice that of 316 stainless (590 degrees Celsius), even though their thermal expansion and specific heat capacity numbers are comparable.

The chemical, petroleum, and marine industries all use the alloy, which has some magnetic properties at room temperature. Up to 1000 F, the Monel K500 Material typically exhibits high tensile strength over a wide temperature range.

Magnets are naturally drawn to and tightly hold ferromagnetic metals. More so than copper, this alloy is resistant to nickel in both reducing and oxidizing environments.

Check monel alloy K500 shaft stock sizes, weight, tolerances, and alloy K500 square bar price per kg in the Middle East and South Korea

Making and welding these bars is straightforward. They are not susceptible to the post-weld carburization and graining that many bars of other grades do.

The products can be made using machining, cold and hot working, and welding. Cold and hot working is both a part of mechanical engineering. Low temperatures are used for “cold working,” while higher temperatures are used for “hot working.” Most DIN 2.4375 Bars can be fused using gas-shielded welding methods like TIG or MIG.

Get DIN 2.4375 bars and K500 round bar in smooth turned/ polished condition in various shapes such as hex, round, square, flat, and hollow

K500 monel alloy rounds can be machined using ferrous alloying methods. However, this is a challenge as the alloy is hardened as it is cut. Pure nickel and alloys such as Monel, K-Monel, Permanickel, and Dunickel can be brazed with inorganic fluxes.

These improved properties – strength and hardness – are achieved by combining aluminum and titanium with the nickel-copper base. The hardened material is machined to hide the sag and improve the surface of the alloy.