SA 213 t11 tube

SA 213 t11 tube

The low ferritic steel alloy of the SA 213 standard makes up the T11 pipe. SA 213 T11 Tube is made up of 0.44-0.65% moly, 0.30-0.60% manganese, & 1-1.50% chromium. By adding to this, it also contains trace amounts of Si, C, K, and Sulphur.

This UNS K11597 T11 Boiler Tube has high oxidation and corrosion-resistant features. The tube is very robust and comes in dimensions 6.35 millimeters OD and 101.6 millimeters OD. Superior mechanical qualities are included in the ASTM A213 T11 Seamless Tube.

Such pipes have a required yield point of 205Mpa and a required tensile strength of 415Mpa. Beveled, basic, and connected piping terminals are available for these tubes.

Verified Supplier

Get suppliers of ASTM a213 t11 seamless tube in UAE and haggle for a good deal. compare ASTM a213 t11 vs t22

SA 213 T11 tube specification


SA 213 T11 Tube Specification

SA 213 T11 tube size range T11 tube length T11 boiler tube equivalent & other trade name
  • Nominal pipe size – 1/8” to 5” NPS
  • Wall thickness: 0.500″

For cut to size material please contact above listed SA 213 T11 tube suppliers in UAE & get a quick quote

  • 6 meters
  • 12 meters
  • Single random lengths (4 – 8 meters)
  • Double random lengths (8 – 13 meters)
  • Custom length or cut to length to save wastage
  • DIN 1.7338
  • UNS K11597
  • Heater Tube – ASTM A213 Gr T11
  • Trade Name: 1 1/4 Chrome, 1 1/4 Cr-1/2Mo
  • Seamless pipe: ASTM A335 Gr P11
ASTM A213 T11 material SA 213 T11 hot formed tubes tempering temperature UNS K11597 A213 T11 tube condition of delivery
  • Alloy Steel
  • Chrome Moly Alloy
  • ASTM A213 T11 Seamless Tube
  • 650°C
  • 1200°F
  • NBK – Normalized
  • BKW – Soft/ Cold-finished
  • BK- Hard/ Cold-finished
  • GBK – Annealed
Manufacturing method of A213 T11 seamless tube SA 213 Gr T11 tube required quality test SA213T11 tube applications & uses
  • Cold drawn seamless low alloy A213 T11 tube
  • Hot finished seamless UNS K11597 A213 T11 tube

Contact verified SA 213 T11 tube suppliers listed above, they also supplied T11 tube material in Saudi Arabia, UAE, Bahrain & Qatar, contact them directly for the best price

  • Bend Test
  • Hardness test
  • Tensile mechanical test
  • Nondestructive Electric Test
  • Flattening test
  • Hydrostatic Test

All above SA 213 T11 tube suppliers are verified, they offer third party inspection, MTC EN 10204 3.1 and IBR certificate with delivery in UAE & Middle east countries

  • Boilers for super heaters
  • Boiling water tube
  • Heat exchangers
  • High pressure steam pipeline
  • Superheated pipelines
  • Power generation
  • Fossil fuel plants
  • Aircraft industry
  • Electric power plants
European standard of Alloy Steel SA 213 T11 seamless ferritic alloy tubes T11 Steel tube approved ex-stock Heat treatment methods of A213 T11 tube
  • EN 10216-2 (IBR Approved SA213T11 seamless tube)
  • EN 10217-2 (SA 213 Gr T11 welded tube)
Above listed SA 213 T11 tube suppliers offer ex-stock in in middle east with the following approvals

  • KOC
  • Petronas
  • ADNOC
  • Saudi Aramco
  • Petrobras
  • PDO
  • Pemex
  • Qatar Gas
  • PDVSA
  • Spray rust removal
  • Cleaning
  • Acid cleaning
  • Tempering
  • Annealing
  • Quenching

Do you require a UNS k11597 t11 boiler tube with a price list for your project? Buy it from Middle East stockist. Identify how much pressure can take alloy steel t11 boiler tube.

Shipping time of ASME SA213 T11 in middle east countries

Looking to buy UNS K11597 A213 T11 in Middle east? Check estimated delivery of EN 10216-2 10CrMo5-5 to your nearby port

Middle East country name List of Port SA 213 T1 tube Import days from Europe
(Italy, Spain, Sweden, Norway)
SA213 T11 material procurement from USA
(North America)
Estimated delivery of SA213T11 tube from Indian manufacturers Estimated delivery of A213 T11 tube from China
Turkey
  • Port Akdeniz Antalya Turkey
  • Haydarpasa Port Turkey
  • Izmir Port Turkey
13-14 14-16 16-18 19-21
Yemen
  • Puerto de Aden Port Yemen
  • Al-Hudaydah Port Yemen
25-26 24-26 14-16 22-24
Israel
  • Port of Eilat Israel
  • Port of Haifa Israel
  • Hadera port Israel
15-16 14-20 7-8 18-20
Qatar
  • Doha Port Qatar
  • Hamad Port Qatar
26-28 25-30 4-5 18-20
Kuwait
  • Shuaiba Port Kuwait
  • Shuwaikh Port Kuwait
  • Doha Port Kuwait
27-28 31-33 5-7 26-40
Cyprus
  • Port of Famagusta Cyprus
  • Limassol Port Cyprus
12-14 25-30 8-12 15-20
Oman
  • Al Sultan Qaboos Port Ship, Mutrah, Oman
  • Salalah Port Oman
  • Sultan Qaboos Port Oman
22-23 20-22 2-3 15-17
Egypt
  • Alexandria Port Egypt
  • Port of ADABIYA Egypt
  • Sokhna Port Egypt
  • Port Said Egypt
  • Port of Abu Qir Egypt
  • Dekheila Port Egypt
  • Safaga Port Egypt
18-20 15-20 12-15 15-18
Saudi Arabia (KSA)
  • Jubail Commercial Port Saudi Arabia
  • Gizan Port Saudi Arabia
  • Jeddah Islamic Port, Saudi Arabia
16-18 30-40 5-6 15-18
UAE (Dubai)
  • Khalifa Port Dubai (UAE)
  • Mina Rashid Port Dubai (UAE)
  • Fujairah Port Dubai (UAE)
  • Jebel Ali Port Dubai (UAE)
  • Hamriyah Port Dubai (UAE)
  • Zayed Port
    Dubai (UAE)
  • Al Hamriya Port Dubai (UAE)
24-26 5-10 8-10 20-25
Bahrain
  • Manama Harbour Port Bahrain
  • Sitra Port Bahrain
  • Mina Salman Port Bahrain
  • Al Muharraq Port Bahrain
  • Khalifa Bin Salman Port Bahrain
35-37 31-33 5-6 20-21
Jordan
  • Port of Aqaba Jordan
24-26 13-16 8-10 25-30

Notes:

  • Above is the approximate IBR Approved SA213T11 high pressure tube seamless tube shipping delivery schedule in UAE and other middle east countries, you can contact above listed SA 213 T11 Tube suppliers in UAE for the exact shipping time.
  • Import time of UNS K11597 T11 Boiler Tube in UAE depend upon the Ex- stock.
  • If the SA 213 T11 heat exchanger tube material not available in UAE then you can view the shipping estimate to import the T11 Boiler Tube in Middle east

Leading manufacturers of SA213 T11 superheater tubes

A213 T11 manufacturers Origin / Country
BENTELER SHREVEPORT, USA
MAHARASHTRA SEAMLESS LTD. INDIA
JSW INDIA
HYUNDAI HYSCO KOREA
ISMT INDIA
BUTTING GERMANY
SEAH KOREA
JFE JAPAN
ARCELORMITTAL UK
TUBOS SPAIN
TENARIS ITALY
VALCOVNY TRUB CHOMUTOV CZECHIA (Europe)

IBR Certified ASME SA213 T11 seamless tubing important elements comparison

Elements SA 213 T11 Boiler Tube SA 213 T12 SA 213 T22 SA 213 T91
Chromium / chrome (Cr) 1.00-1.50 0.80-1.25 1.90-2.60 8.0-9.5
Molybdenum/ Moly (Mo) 0.44-0.65 0.44-0.65 0.87-1.13 0.80-1.05
Phosphorus (p) 0.025 0.025 0.025 0.02
Sulfur (S) 0.025 0.025 0.025 0.01
Silicon (Si) 0.50-1.00 0.5 0.5 0.20-0.50
Carbon (C) 0.05-0.15 0.05-0.15 0.05-0.15 0.07-0.14
Manganese (Mn) 0.30-0.60 0.30-0.61 0.30-0.60 0.30-0.60
Yield strength ≥205 MPa
  • 32 KSI
  • 220 MPa
≥220 MPa
  • 60 KSI
  • 415 MPa
Tensile strength ≥415 MPa
  • 60 KSI
  • 415 MPa
≥415 MPa
  • 85 KSI
  • 585 MPa
Temperature range 650°C 650-730°C 675°C 590°C

Mill tolerance for T11 tube material wall thickness

SA213 T11 NPS or DN A213 T11 Tolerance
(
% from Specified)
Over Under
  • 1/8 NPS to 2 1/2 NPS [6 to 65] inclusive
  • all t/D ratios
20.0% 12.5%
  • Above 2 1/2 NPS [65]
  • t/D < or = 5%
22.5% 12.5%
  • Above 2 1/2 NPS [65]
  • t/D > 5%
15.0% 12.5%
Notes:

  • t means = Specified ASTM A213 T11 wall thickness
  • D means = Specified SA213 T11 outside diameter

Allowable or permissible variation of A213 gr T11 boiler tube OD

T11 Boiler Tube NPS or DN Over Under
inch mm inch mm
  • 1/8 NPS to 1 1/2 NPS [6 to 40], including
1/64 (0.015) 0.40 1/64 (0.015) 0.40
  • Over 1 1/2 NPS to 4 NPS [40 to 100], including
1/32 (0.031) 0.79 1/32 (0.031) 0.79
  • Over 4 NPS to 8 NPS [100 to 200], including
1/16 (0.062) 1.59 1/32 (0.031) 0.79
  • Over 8 NPS to 12 NPS [200 to 300], including
3/32 (0.093) 2.38 1/32 (0.031) 0.79
  • Over 12 NPS [300]
+/- 1% of the specified 1.7338 outside diameter

Ferritic low alloy steel SA 213 T11 round tube marking

Marking heading
Grade/ material
Length
Schedule
Manufacturer’s Heat Number
Test name
  • S1 – SA213 T11 Superheater Tubes Analysis
  • S2 – T11 Steel Cold Drawn Tube Transverse Tension Test
  • S3 – Flattening Test of A213 T11 heater tube
  • S4 – Etching Tests & Metal Structure
  • S5 – Photomicrographs
  • S6 – 1.7338 Furnace Tubes Photomicrographs for Individual Pieces
  • S7 – Alternative Heat Treatment – only for ASTM A213 T91 (type 1 and 2)
Indicate T11 steel test method
  • Test Pressure – if Hydrostatic yes, Nondestructive No
  • NDE – if Hydrostatic No, Nondestructive Yes
  • NH – if Hydrostatic No, Nondestructive No
  • Test Pressure/NDE – if Hydrostatic yes, Nondestructive yes

SA 213 T11 tube chemical composition

Grade Mo Mn C≤ P≤ S≤ Si≤
T11 0.44~0.65 0.30~0.60 0.05~0.15 0.025 0.025 0.50~1.0

Mechanical properties of T11 boiler tube

Grade Yield Strength, MPa Tensile Strength, MPa Elongation, % Hardness, HB
T11 205 min 415 min 30 min
  • 163 HBW
  • 85 HRB

Heat treatment requirements of ASTM A213 gr T11 seamless ferritic alloy tubes

Grade UNS
Number
Heat Treat Type Subcritical Annealing or Tempering,
min or range ºF [ºC]
Austenitizing/ Solutioning,
min or range ºF [ºC]
Cooling Media
T11 K11597 Full or Isothermal anneal
normalize and temper 1200 [650]

ASTM A213 T11 equivalent

Standards Country SA 213 T11 Tube
UNS North America K11597
WNR Russia 1.7335
ASTM America A213
ASME Australia SA 213
JIS Japan
BS United Kingdom
GOST Russia GOST 550-75
AFNOR France
EN Europe EN 10216-2
AS Australia
DIN German 1.7335

SA 213 T11 Tube Properties

Seek out an importer of sa 213 gr t11 tubing who offers MTC and the ability to cut to length, see t11 tube hot vs cold rolling procedures

The extreme heat of 2000 ° Celsius is used to roll or form the A213 T11 Hot Finished Tube. Manufactured in dimensions up to 22.5 meters, such tubing has exceptional flanging & bending characteristics. After the hot-rolling procedure, T11 Steel Cold Drawn Tube is cold formed. To enhance their performance in effective usage, tubing is given the correct qualities and coatings throughout this operation.
The complete or adiabatic anneal, normalize, and tempering processes are used for grading T11 thermal processing. For cold-formed pipes, allowable deviations from the stated mean wall width must not exceed +/- 10% of that value.

SA 213 Gr T11 tubing has silicon content that is equal to or lower than SA 213 T22 tubing. T22 seamless tubing as compared with T11 seamless tubing contains a high amount of chromium and molybdenum. Both SA213 T11 material and SA213 T22 materials share similar mechanical characteristics, such as tensile strength, yield strength, % elongation, and hardness. ASTM 213 T11 Seamless tubing requires a temperature of around 1200 degrees Fahrenheit for subcritical annealing, tempering, or annealing (650 degree Celsius). T22 tubing needs to be heated to roughly 1250 degrees Fahrenheit to reach its subcritical, annealing, or tempering temperatures (675 degree Celsius).

SA 213 Gr T11 tubing has silicon content that is equal to or lower than SA 213 T22 tubing. T22 seamless tubing as compared with T11 seamless tubing contains a high amount of chromium and molybdenum. Both SA213 T11 material and SA213 T22 materials share similar mechanical characteristics, such as tensile strength, yield strength, % elongation, and hardness. ASTM 213 T11 Seamless tubing requires a temperature of around 1200 degrees Fahrenheit for subcritical annealing, tempering, or annealing (650 degree Celsius). T22 tubing needs to be heated to roughly 1250 degrees Fahrenheit to reach its subcritical, annealing, or tempering temperatures (675 degree Celsius).

UNS K11597 T11 boiler tubes are low-maintenance and have a long-life expectancy even under conditions of extreme pressure and temperature. A Little Bore Pipe made of Alloy Steel SA 213 T11 is simple to install and needs minimal connectors. Since the connection doesn’t have any abrupt curves, these pipes don’t exhibit pressure dips. The EN 10216-2 10CrMo5-5 Boiler Fin Tube is a robust tubing with a minimum tensile strength of 415 MPa as well as a minimum yield strength of 205 MPa, making it capable of withstanding extreme temperatures and pressures. High creep-rupture resistance is among the most crucial qualities of alloys used during pressure container manufacturing & power plant engineering.

Are you searching in Dubai for reputable sa213 t11 material distributors? find out are a213 t11 hot finished tube leak-proof.

The ASME sa213 t11 seamless piping does indeed have no leaks and is simple to maintain. Check for leaks in continuous steel pipe on a routine basis, either with your naked eye or by observing a pressure drop. The measured maximum test pressure of 120 Mpa satisfies all pressure water required specifications for continuous tubes in boilers, superheaters, and heat exchangers.
To provide a leak-free tubing connection, the SA 213 T11 Heat Exchanger Tube is built robustly from premium-grade materials.
In so many industries, the Mild Alloy A213 T11 Large Size Pipe is the preferred material. Despite having little alloying ingredients, these tubes are quite strong and have superior mechanical qualities.

T11 steel cold drawn tube is offered in custom sizes and complies with all international standards. Look how should I maintain 1.7338 furnace tubes?

The T11 Boiler Tube is relatively simple to handle and maintain. They can withstand a broad range of pressure and temperature, but we must be careful to keep those values within tolerable or practical limits.
For the pipes to exhibit their long-lasting property, we must create an environment that is ideal. These pipes’ good mechanical qualities make them easy to handle or install them. These pipes are both seamless and welded. Seamless pipes are less likely to leak and are simple to maintain.
These pipes are ideal for usage in a variety of sectors since they are very comfortable to use and have outstanding characteristics